In the paper the results of experimental research of the process of flow forming of cylindrical drawpieces were presented. The drawpieces were made of the 3.1 mm thick AMS 5596 sheet by drawing process. Tests were performed on two-roller metal spinning machine of a vertical axis Leifeld SFC 800 V500. The main purpose of this research was to determine the relationship between relative thickness reduction and the mechanical properties of tested material. Knowledge of these dependencies is especially useful in designing machines’ components manufactured by flow forming, in the selection of parameters of realization of this technological process as well. Mechanical properties were determined on the basis of uniaxial tensile of the micro samples obtained from the drawpieces: (I) after cold flow forming, (II) after cold flow forming and in-process heat treatment. Obtained results were shown graphically in the diagrams and their analysis was carried out. In addition, the microstructure of the sheet material tested after drawing and flow forming is presented.
The article reports the results of research on the influence of the alternate intermittent deformation of specimens by a torsion method on the Bauschinger effect in the Zr-1%Nb zirconium-based alloy. Tests were carried out using an STD 812 torsion plastometer. Based on the tests carried out, diagrams have been plotted, which represent the influence of the pre-deformation magnitude, the temperature of heat treatment prior to deformation, and deformation rate on the variation in the values of the flow stress and yield strength of the alloy under study. Conditions have been defined, in which larger magnitudes of plastic deformation of Zr-1Nb% alloy material can be used during its cold plastic working.